Structuring of LTCC Substrates by a Combination of Pressure-Assisted Sintering and Hot Embossing

  • A novel technology for the structuring of low temperature co-fired ceramic (LTCC) surfaces is introduced. The commercial LTCC Ceramtape GC is shaped in a zero-shrinkage process by embossing a glass-like carbon mold into the softened LTCC during pressure-assisted sintering. Diverse raised and lowered structures including rings, grids, and characters were fabricated. It was found that de-airing of mold cavities is crucial for the molding of embossments. De-airing is possible through pore channels in the LTCC if embossing is performed at intermediate temperatures. The influence of LTCC viscosity on the mold filling behavior during the formation of raised structures is discussed. For accurate molding and proper densification of the LTCC, hot embossing with 0.41 MPa at 775 °C and subsequent heating under load to 850 °C is proposed. Embossing of precise, 40 µm deep circular cavities and 50 µm high raised bars and characters is demonstrated. Thereby, the high potential of the hot-embossingA novel technology for the structuring of low temperature co-fired ceramic (LTCC) surfaces is introduced. The commercial LTCC Ceramtape GC is shaped in a zero-shrinkage process by embossing a glass-like carbon mold into the softened LTCC during pressure-assisted sintering. Diverse raised and lowered structures including rings, grids, and characters were fabricated. It was found that de-airing of mold cavities is crucial for the molding of embossments. De-airing is possible through pore channels in the LTCC if embossing is performed at intermediate temperatures. The influence of LTCC viscosity on the mold filling behavior during the formation of raised structures is discussed. For accurate molding and proper densification of the LTCC, hot embossing with 0.41 MPa at 775 °C and subsequent heating under load to 850 °C is proposed. Embossing of precise, 40 µm deep circular cavities and 50 µm high raised bars and characters is demonstrated. Thereby, the high potential of the hot-embossing process for micro-patterning of LTCC is illustrated.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Brandt, Rabe, JCST,2015.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Björn MiellerORCiD, Torsten Rabe
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of Ceramic Science and Technology
Jahr der Erstveröffentlichung:2015
Jahrgang/Band:06
Ausgabe/Heft:04
Erste Seite:273
Letzte Seite:278
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:glass-like carbon; hot-embossing; low temperature co-fired ceramics; pressure-assisted sintering
DOI:10.4416/JCST2015-00051
Bemerkung:
Geburtsname von Mieller, Björn: Brandt, B. -  Birth name of Mieller, Björn: Brandt, B.
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:16.03.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.