Damaging effect of admixtures used in crop protection products on high density polyethylene packaging material
- The phenomenon of environmental stress cracking is still a major issue in materials engineering as well as from a scientific perspective. Especially in the case of packaging materials made of high-density polyethylene, assessing the potential of premature damage due to environmental stress cracking is complex because of the large number of components in possible liquid filling goods. As a first guideline, the well-known effect of detergents and dispersants is usually considered, but the interplay with other components, such as organic solvents is often unknown. Particularly challenging in this respect are crop protection products, consisting of several different admixtures in addition to the biologically active ingredients. This study is based on two model liquids representing these admixtures that were established for testing in this context. The model liquids as well as their constituting components were used as liquid media in the Full Notch Creep Test to characterize theThe phenomenon of environmental stress cracking is still a major issue in materials engineering as well as from a scientific perspective. Especially in the case of packaging materials made of high-density polyethylene, assessing the potential of premature damage due to environmental stress cracking is complex because of the large number of components in possible liquid filling goods. As a first guideline, the well-known effect of detergents and dispersants is usually considered, but the interplay with other components, such as organic solvents is often unknown. Particularly challenging in this respect are crop protection products, consisting of several different admixtures in addition to the biologically active ingredients. This study is based on two model liquids representing these admixtures that were established for testing in this context. The model liquids as well as their constituting components were used as liquid media in the Full Notch Creep Test to characterize the environmental stress cracking behavior of a typical high-density polyethylene. Complementary to the time-to failure of a notched specimen obtained from these tests, the crack opening was monitored optically, and the fracture surface was analyzed post-failure by laser scanning microscopy as well as scanning electron microscopy. Based on the results, the effect of various surfactants as well as the influence of organic solvents on environmental stress cracking are discussed.…
Autor*innen: | Maximilian ThuyORCiD, Ute NiebergallORCiD, H. Oehler, I. AligORCiD, Martin BöhningORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Polymer Testing |
Jahr der Erstveröffentlichung: | 2022 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.3 Polymere Verbundwerkstoffe | |
7 Bauwerkssicherheit | |
7 Bauwerkssicherheit / 7.5 Technische Eigenschaften von Polymerwerkstoffen | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | Elsevier Ltd. |
Verlagsort: | Amsterdam |
Jahrgang/Band: | 114 |
Aufsatznummer: | 107672 |
Erste Seite: | 1 |
Letzte Seite: | 16 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Crack opening displacement; Crop protection products; Environmental stress cracking; Fracture surface analysis; Full notch creep test; High-density polyethylene |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.1016/j.polymertesting.2022.107672 |
URN: | urn:nbn:de:kobv:b43-554631 |
ISSN: | 0142-9418 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY-NC-ND - Namensnennung - Nicht kommerziell - Keine Bearbeitungen 4.0 International |
Datum der Freischaltung: | 10.08.2022 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 19.10.2022 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |