Nucleation and growth of sulfur phases in grain boundaries

  • Ferritic-martensitic high temperature alloys are used as building components for different power plant technologies. Depending on the type of fuel, the used power plant materials are exposed to different temperatures and reactive atmospheres containing e.g. CO2, O2, or SO2. Despite the sulfur chemistry is commonly present as an impurity in fossil or bio fuels; its role in high temperature corrosion is not entirely understood. During high temperature corrosion, high-alloyed steels often show sulfur precipitates with the ignoble alloy component(s) along grain boundaries within the base material. Sulfur precipitates are known to seriously influence the mechanical properties of the building component. In the case of VM12 and T92 steels, sulfur phases penetrate the base material along grain boundaries during the corrosion under oxyfuel atmosphere up to 20 µm within the first 960h (Fig. 1a). Figure 1a shows the oxide scale and (Cr, Mn, Fe)xSy grain boundary precipitates in the base materialFerritic-martensitic high temperature alloys are used as building components for different power plant technologies. Depending on the type of fuel, the used power plant materials are exposed to different temperatures and reactive atmospheres containing e.g. CO2, O2, or SO2. Despite the sulfur chemistry is commonly present as an impurity in fossil or bio fuels; its role in high temperature corrosion is not entirely understood. During high temperature corrosion, high-alloyed steels often show sulfur precipitates with the ignoble alloy component(s) along grain boundaries within the base material. Sulfur precipitates are known to seriously influence the mechanical properties of the building component. In the case of VM12 and T92 steels, sulfur phases penetrate the base material along grain boundaries during the corrosion under oxyfuel atmosphere up to 20 µm within the first 960h (Fig. 1a). Figure 1a shows the oxide scale and (Cr, Mn, Fe)xSy grain boundary precipitates in the base material for a T92 steel aged for 960h under oxyfuel atmosphere. Figure 1b shows a thin oxide scale with nodules and also sulfur precipitates of (Fe, Cr)xSy along grain boundaries of the base material for a Fe13Cr model alloy aged for 24h under SO2 atmospheres. After 24h, sulfur precipitates already reached a depth of ca. 15 µm. The present work shows the corrosion behavior of Fe-Cr model alloys with Cr-contents similar to technical steels up to 13 wt%, aged under oxyfuel (27H2O/60CO2/1SO2/10N2/2O2) and SO2 atmospheres in the temperature range of 550 °C < T < 700 °C and for different time scales between 24 h < t < 960 h. During aging, the reactive gases were added when the experimental temperature was reached. To focus on the reaction of the intended elements Fe, Cr, S, and O, model alloys of high purity are used. Transport depths of sulfur and the nucleation of the precipitates are discussed for both, model alloys and technical steels.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • MSE_Nuetzmann.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Kathrin Nützmann
Koautor*innen:Maria Mosquera Feijoo
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2016
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik
Freie Schlagwörter:Corrosion; Sulfidation; Sulfide
Veranstaltung:Materials Science & Engineering
Veranstaltungsort:Darmstadt, Germany
Beginndatum der Veranstaltung:27.09.2016
Enddatum der Veranstaltung:29.09.2016
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:14.10.2016
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.