Fracture on microscale of fiber reinforced composites

  • Failure of composite materials is initiated by fracture processes on microscale, especially by interfacial debonding. Failure processes taking place on microscale are studied by single fiber experiments. This is, single fibers embedded in tensile specimen are loaded under various off-axis angles. Starting at microdefects interface cracks propagate circumferentially as well as longitudinally, depending on the loading angle. In addition, finite element simulations of interfacial crack propagation around single fibers as well as fibers embedded in a hexagonal composite are shown based on linear elastic fracture mechanics. The course of the energy release rate is given in dependence of the fiber volume fraction.

Volltext Dateien herunterladen

  • Imperial College_Marotzke Oct 12.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Christian Marotzke
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2016
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.0 Abteilungsleitung und andere
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Composites; Epoxy resin; Fracture surfaces; Micromechanics
Themenfelder/Aktivitätsfelder der BAM:Material
Veranstaltung:Seminar
Veranstaltungsort:Imperial College, London, UK
Beginndatum der Veranstaltung:12.10.2016
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:18.10.2016
Referierte Publikation:Nein