Structural integrity of sandwich structures in fire: an intermediate-scale approach

  • A test set-up in intermediate scale was conceived to investigate the structural integrity of materials under fire. The task was to develop a realistic test scenario targeting component-like behaviour. Carbon-fibre-reinforced sandwich specimens (500 X 500 X 20 mm) were used to examine failure mechanisms, times to failure and critical failure loads under compression. Fire tests were performed with fully developed fire applied to one side of the specimen by an oil burner. In a first test series, the applied load was varied, but the fully developed fire remained unchanged. In general, times to failure were short. Decreased load levels resulted in prolonged times to failure and led to a different failure mechanism. Results obtained in the test series were compared with a bench-scale study (150 X 150 X 20 mm) investigating identical material. The comparison clearly revealed the influence of size on the time to failure and the load-bearing capacity.

Volltext Dateien herunterladen

  • Structural integrity of sandwich structures in fire.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Andreas Hörold, Bernhard SchartelORCiD, Volker TrappeORCiD, Manfred Korzen, Maurice Naumann
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Composite interfaces
Jahr der Erstveröffentlichung:2013
Verlag:VSP
Verlagsort:Zeist
Jahrgang/Band:20
Ausgabe/Heft:9 (Special Issue: ECCM15: Part 3)
Erste Seite:741
Letzte Seite:759
Freie Schlagwörter:Carbon-fibre-reinforced plastics; Composites; Fire testing; Fully developed fire; Structural integrity
DOI:10.1080/15685543.2013.816620
ISSN:0927-6440
ISSN:1568-5543
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:28.11.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.