Real-time observation of high- temperature gas corrosion in dry and wet SO2-containing atmosphere
- Sulfur and water have a fundamental impact on the corrosion rate and potential failure of materials. It is therefore necessary to understand the mechanisms, rates, and potential means of transport, as well as the reactions of these elements with an alloy. This paper investigates the effect of water vapor in the initial stages of SO2 corrosion of an Fe-9Cr-0.5Mn model alloy at 650°C in situ under laboratory conditions using energy-dispersive x-ray diffraction analysis. Two separate experiments were run, one with a 99.5% Ar + 0.5% SO2 atmosphere and one with a 69.5% Ar + 0.5% SO2 + 30% H2O atmosphere. With a wet atmosphere, the alloy formed a scale with decreasing oxygen content towards the scale–alloy interface. Sulfides were identified above and below a (Fe, Cr)3O4 layer in the inner corrosion zone. In contrast to this, the overall scale growth was slower in a dry SO2 atmosphere.
Autor*innen: | Florian Falk, M. Menneken, Christiane Stephan-ScherbORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | JOM The Journal of The Minerals, Metals & Materials Society (TMS) |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | Springer |
Verlagsort: | New York |
Jahrgang/Band: | 71 |
Erste Seite: | 1 |
Letzte Seite: | 6 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik | |
Freie Schlagwörter: | Early oxidation; Early sulfidation; Ferritic steels |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
Material | |
Material / Degradation von Werkstoffen | |
DOI: | 10.1007/s11837-019-03335-9 |
URN: | urn:nbn:de:kobv:b43-472844 |
URL: | https://link.springer.com/article/10.1007/s11837-019-03335-9#enumeration |
ISSN: | 1047-4838 |
ISSN: | 1543-1851 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY - Namensnennung 4.0 International |
Datum der Freischaltung: | 30.01.2019 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 11.04.2019 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |