Fatigue loading of sandwich shell test specimens with simulated production imperfections and in-situ NDT
- A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated.
Autor*innen: | Volker TrappeORCiD |
---|---|
Koautor*innen: | Dustin Nielow |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.3 Polymere Verbundwerkstoffe | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik |
Freie Schlagwörter: | Fatigue of sandwich shell structures; Non-destructive testing; Wind turbine blades |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
Veranstaltung: | 7. International Conference on Fatigue of Composites |
Veranstaltungsort: | Vicenza, Italy |
Beginndatum der Veranstaltung: | 04.07.2018 |
Enddatum der Veranstaltung: | 06.07.2018 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 20.12.2019 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |