Influence of prestraining on the aging response of an Al-Cu-Li alloy
- The influence of prestraining on the aging response of an Al-Cu-Li alloy is investigated by preparation of different strain states (3 %, 4 %, 6 %) of the initial aging state. The Brinell hardness of the subsequently aged samples (up to 60 h aging time) was measured and it was found that the increasing dislocation concentration in the 3 different initial states leads to faster hardness increases and slightly higher maximum hardness.
Autor*innen: | Christian Rockenhäuser, Benjamin Piesker, Daniel Heidl, Birgit SkrotzkiORCiD |
---|---|
Dokumenttyp: | Beitrag zu einem Tagungsband |
Veröffentlichungsform: | Graue Literatur |
Sprache: | Deutsch |
Titel des übergeordneten Werkes (Deutsch): | Microscopy Conference 2019 (MC2019) - Proceedings |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.2 Metallische Hochtemperaturwerkstoffe | |
Verlag: | Deutsche Gesellschaft für Elektronenmikroskopie (DGE) |
Verlagsort: | Dresden |
Erste Seite: | 186 |
Letzte Seite: | 187 |
Freie Schlagwörter: | Al-Cu-Li alloys; coarsening; hardness |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
Veranstaltung: | Microscopy Conference 2019 (MC2019) |
Veranstaltungsort: | Berlin, Germany |
Beginndatum der Veranstaltung: | 01.09.2019 |
Enddatum der Veranstaltung: | 05.09.2019 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 12.09.2019 |
Referierte Publikation: | Nein |