Failure of fiber reinforced composites – role of the matrix behaviour and the interface strength
- Failure of fiber reinforced composites initiates at microdefects in the matrix or at the interface. The interface strength is calculated from the stress field directly before crack initiation by nonlinear finite element simulations. Large deformations and plastic material behaviour are taken into account. Microscopical inspections of the fibers after failure show only small regions with adhering matrix material. This indicates that the interface strength is below the matrix strength.
Autor*innen: | Christian Marotzke |
---|---|
Koautor*innen: | Titus Feldmann |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2016 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | composites; fracture mechanics; nonlinear material behaviour |
Veranstaltung: | 2nd International Conference on Mechanics of Composites |
Veranstaltungsort: | Porto, Portugal |
Beginndatum der Veranstaltung: | 12.07.2016 |
Enddatum der Veranstaltung: | 14.07.2016 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 27.07.2016 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |