Failure of fiber reinforced composites under multiaxial stresses on microscale

  • The failure of composites is initiated by imperfections on microscale. The interface between fiber and matrix is a key parameter concerning failure initiation. In order to get an improved understanding of local failure processes a fracture mechanical analysis of interfacial failure in a composite ply under transverse stresses is performed. The mixed mode energy release rate is calculated. In addition the failure of interfaces under cyclic loading is studied on a single fiber model. The quasistatic debonding process is compared with the interfacial failure under fatigue loading. It is shown that the tan delta can be used as an indicator for the damage propagation.

Volltext Dateien herunterladen

  • ICMFF11_Paper Marotzke N.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Christian Marotzke, Titus Feldmann
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Proceedings of ICMFF11
Jahr der Erstveröffentlichung:2016
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.0 Abteilungsleitung und andere
Erste Seite:1
Letzte Seite:8
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:failure mechanics; failure mechanisms; micromechanics; multiaxial loading
Themenfelder/Aktivitätsfelder der BAM:Material
Veranstaltung:ICMFF11
Veranstaltungsort:Sevilla, Spain
Beginndatum der Veranstaltung:01.06.2016
Enddatum der Veranstaltung:03.06.2016
Verfügbarkeit des Volltexts:Volltext-PDF im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:18.10.2016
Referierte Publikation:Nein