Impact of thermal loads on the damage onset of fiber reinforced plastics

  • In this study, quasi-static material tests on unidirectional and multi-angle glass fiber reinforced epoxy laminates at ambient temperatures from -213 K to 353 K (-60 °C to +80 °C) are performed. In addition, neat resin is investigated under tension and compression loads at different temperatures. The coefficient of thermal expansion is determined for neat resin and unidirectional reinforced specimens. The dependence of the resin’s thermomechanical properties on the ambient temperature is shown. The point of damage onset at which first cracks appear within the matrix under quasi-static loading is investigated by means of optical grey scale analysis. The correlation between damage onset and effective matrix stress at different ambient temperatures is identified. An approach for the calculation of thermomechanical loads and the prediction of the damage onset by means of inverse calculations is presented. The impact of the strain blocking effect of the matrix is considered as well asIn this study, quasi-static material tests on unidirectional and multi-angle glass fiber reinforced epoxy laminates at ambient temperatures from -213 K to 353 K (-60 °C to +80 °C) are performed. In addition, neat resin is investigated under tension and compression loads at different temperatures. The coefficient of thermal expansion is determined for neat resin and unidirectional reinforced specimens. The dependence of the resin’s thermomechanical properties on the ambient temperature is shown. The point of damage onset at which first cracks appear within the matrix under quasi-static loading is investigated by means of optical grey scale analysis. The correlation between damage onset and effective matrix stress at different ambient temperatures is identified. An approach for the calculation of thermomechanical loads and the prediction of the damage onset by means of inverse calculations is presented. The impact of the strain blocking effect of the matrix is considered as well as residual thermal stresses due to curing and resin shrinkage.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • IMPACT OF THERMAL LOADS ON THE DAMAGE ONSET OF FIBER REINFORCED PLASTICS.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:David Kraus, Volker TrappeORCiD
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):ICCM21 - 21th International conference on composite materials (Proceedings)
Jahr der Erstveröffentlichung:2017
Herausgeber (Institution):ICCM
Erste Seite:1
Letzte Seite:12
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Composite; Damage onset; Fatigue; Fiber reinforced plastics; Thermomechanics
Veranstaltung:ICCM21 - 21th International conference on composite materials
Veranstaltungsort:Xi'an, China
Beginndatum der Veranstaltung:20.08.2017
Enddatum der Veranstaltung:25.08.2017
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:22.09.2017
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.