Infinite life of CFRP evaluated nondestructively with X-ray-refraction topography

  • CFRP are more and more used in modern civil aircrafts hence the whole fuselage is made of this material (B787; A350). Due to strict certification Standards finally the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles. The first inter-fiber failure was evaluated non-destructively by the fatigue tests accompanying X-ray-refraction topography altemately and in-situ mechanical loading. The basic idea of the investigation is represented in fig. 1. At low load levels it could not be assumed the total failure of the samples. Hence accompanying non-destructive testing (NDT) is mandatory to get information about the damage state of the material.

Volltext Dateien herunterladen

  • Infinite life of CFRP evaluated nondestructively with X-ray-refraction topography.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Volker Trappe, Hans-Peter Ortwein, Stefan Hickmann
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):ICCM19 - 19th International conference on composite materials (Proceedings)
Jahr der Erstveröffentlichung:2013
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.3 Mechanik der Polymerwerkstoffe
Herausgeber (Institution):Canadian Association for Composite Structures and Materials
Erste Seite:1
Letzte Seite:8
Freie Schlagwörter:Carbon fibre reinforced plastics (CFRP); Damage mechanics; Non-destructive testing (NDT); Very high cycle fatigue (VHCF); X-ray refraction
Veranstaltung:ICCM19 - 19th International conference on composite materials
Veranstaltungsort:Montreal, Canada
Beginndatum der Veranstaltung:28.07.2013
Enddatum der Veranstaltung:02.08.2013
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:14.08.2014