Corrosion of uncoated and alumina coated steel X20CrMoV12-1 in H2O-CO2-O2 and air at 600 °C

  • Future coal power plants will in case of oxyfuel combustion be operated with altered atmospheres. Hence, corrosion attack might become more severe and steels have to be protected. An alumina-sol was used to coat X20CrMoV12-1 (X20) with alumina to test the protection. Testing was performed at 600 °C in flowing H2O–CO2–O2 and static laboratory air for 1000 h. Oxidation under air is minor compared to exposure in oxyfuel atmosphere. In both cases a multilayered oxide (hematite, magnetite, spinel) was formed on uncoated steels. Carburization appeared on uncoated X20 in H2O–CO2–O2. The coating demonstrates a high protection.

Volltext Dateien herunterladen

  • 1-s2.0-S0010938X1200515X-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Wencke Schulz, Marianne NofzORCiD, Michael Feigl, Ilona Dörfel, Romeo Saliwan Neumann, Axel KranzmannORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Corrosion science
Jahr der Erstveröffentlichung:2013
Verlag:Elsevier Ltd.
Verlagsort:Orlando, Fla.
Jahrgang/Band:68
Erste Seite:44
Letzte Seite:50
Freie Schlagwörter:A. Steel; B. SEM; B. STEM; C. Carburization; C. High temperature corrosion; C. Oxide coatings
DOI:10.1016/j.corsci.2012.10.031
ISSN:0010-938X
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:31.01.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.