Residual stress in selective laser melted Inconel 718: Influence of the removal from base plate and deposition hatch length
- The residual stress distribution in IN718 elongated prisms produced by Selective Laser Melting was studied by means of neutron (bulk) and laboratory X-ray (surface) diffraction. Two deposition hatch lengths were considered. A horizontal plane near the top surface (perpendicular to the building direction) and a vertical plane near the lateral surface (parallel to the building direction) were investigated. Samples both in as-built (AB) condition and removed (RE) from the base plate were characterized. While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements. Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulkThe residual stress distribution in IN718 elongated prisms produced by Selective Laser Melting was studied by means of neutron (bulk) and laboratory X-ray (surface) diffraction. Two deposition hatch lengths were considered. A horizontal plane near the top surface (perpendicular to the building direction) and a vertical plane near the lateral surface (parallel to the building direction) were investigated. Samples both in as-built (AB) condition and removed (RE) from the base plate were characterized. While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements. Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulk stress gradients partially disappear after removal from the baseplate.…
Autor*innen: | Tobias Thiede, S. Cabeza, Tatiana MishurovaORCiD, N. Nadammal, Arne KrommORCiD, Johannes Bode, C. Haberland, Giovanni BrunoORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Materials, Performance & Characterization |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.0 Abteilungsleitung und andere | |
8 Zerstörungsfreie Prüfung | |
8 Zerstörungsfreie Prüfung / 8.5 Röntgenbildgebung | |
9 Komponentensicherheit | |
9 Komponentensicherheit / 9.2 Versuchsanlagen und Prüftechnik | |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
Verlag: | ASTM International |
Verlagsort: | USA, West Conshohocken |
Jahrgang/Band: | 7 |
Ausgabe/Heft: | 4 |
Erste Seite: | 717 |
Letzte Seite: | 735 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Additive manufacturing; Coordinate measurement machine; IN718; Laboratory X-ray diffraction; Neutron diffraction; Residual stress; Selective laser melting |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Additive Fertigung | |
DOI: | 10.1520/MPC20170119 |
ISSN: | 2379-1365 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 21.11.2018 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 08.04.2020 |