Axle fracture of an ICE3 high speed train

  • In July 2008 an ICE3 high speed train rated for 330 km/h service speed derailed during departure from Cologne, Central Station, Germany, due to fatigue failure of one of the driving axles. The train was emergency stopped immediately and, due to low travel speed at this point, no serious injuries occurred to passengers. Referring to public interest, the public attorney’s office solicited the German Federal Institute for Materials Research and Testing (BAM) for the analysis of the root cause. No deviations from specification were found in the geometries of the basic parts of the bogie or the wheelset assembly. Inspection of the axle fragments using standard acoustic non-destructive testing (NDT) techniques revealed no additional cracks and no indications of oversized discontinuities. Metallographic and chemical inspection of the axle material and its microstructure revealed all parameters to be acceptable except for an elevated impurity level. The fracture surfaces of the axleIn July 2008 an ICE3 high speed train rated for 330 km/h service speed derailed during departure from Cologne, Central Station, Germany, due to fatigue failure of one of the driving axles. The train was emergency stopped immediately and, due to low travel speed at this point, no serious injuries occurred to passengers. Referring to public interest, the public attorney’s office solicited the German Federal Institute for Materials Research and Testing (BAM) for the analysis of the root cause. No deviations from specification were found in the geometries of the basic parts of the bogie or the wheelset assembly. Inspection of the axle fragments using standard acoustic non-destructive testing (NDT) techniques revealed no additional cracks and no indications of oversized discontinuities. Metallographic and chemical inspection of the axle material and its microstructure revealed all parameters to be acceptable except for an elevated impurity level. The fracture surfaces of the axle fragments were heavily damaged due to some continued travel after final breakage on the high speed line before Cologne Central Station. Extensive visual inspection of the remaining beachmarks was carried out to find the origin of the fatigue crack. The region of the crack origin was located near the axle surface but could not be analysed in detail due to secondary damage. Fatigue was identified as the mechanism of crack growth until final fracture, but the reasons for crack initiation initially remained unclear. Neither standard NDT techniques nor metallography according to the relevant axle specifications were able to identify inclusions in the material that could have served as crack initiation sites. However, discontinuities were detected near the crack origin in micro computer tomography and ultrasonic immersion testing. Subsequent metallographic sample preparation was targeted to specific areas based on the location coordinates of the flaws identified by these NDT techniques. These revealed non-metallic inclusions that were much larger than admissible for the relevant specifications. It is likely that the fatigue crack in the highly loaded axle volume initiated at those non-metallic inclusions.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 1-s2.0-S1350630712002543-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Christian Klinger, Dirk BettgeORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Engineering failure analysis
Jahr der Erstveröffentlichung:2013
Verlag:Elsevier Science Publ.
Verlagsort:Oxford
Jahrgang/Band:35
Erste Seite:66
Letzte Seite:81
Freie Schlagwörter:Fatigue crack; Micro computer tomography; Non-metallic inclusions; Railway axle fracture; Ultrasonic immersion technique
DOI:10.1016/j.engfailanal.2012.11.008
ISSN:1350-6307
ISSN:1873-1961
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:02.12.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.