Vacuum crack growth in alkali silicate glasses
- Crack growth velocity in alkali silicate glasses was measured in vacuum across 10 orders of magnitude with double cantilever beam technique. Measured and literature crack growth data were compared with calculated intrinsic fracture toughness data obtained from Young´s moduli and the theoretical fracture surface energy estimated from chemical bond energies. Data analysis reveals significant deviations from this intrinsic brittle fracture behavior. These deviations do not follow simple compositional trends. Two opposing processes may explain this finding: a decrease in the apparent fracture surface energy due to stress-induced chemical changes at the crack tip and its increase due to energy dissipation during fracture.
Autor*innen: | Tina Waurischk, Stefan ReinschORCiD, T. Rouxel, H. Behrens, J. Deubener, Ralf Müller |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Journal of non-crystalline solids |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.6 Glas | |
Verlag: | Elsevier |
Verlagsort: | Amsterdam |
Jahrgang/Band: | 572 |
Aufsatznummer: | 121094 |
Erste Seite: | 1 |
Letzte Seite: | 8 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Brittle fracture; Calculated intrinsic fracture toughness; Crack growth; Silicate glass |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.1016/j.jnoncrysol.2021.121094 |
ISSN: | 0022-3093 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 30.08.2021 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 23.09.2021 |