Positron annihilation investigation of thermal cycling induced martensitic transformation in NiTi shape memory alloy
- Thermal cycling of a Ni-excess NiTi alloy was conducted between 50 °C and liquid nitrogen temperature to induce martensitic transformations and to reverse them after. The starting point was an annealed and slowly cooled state, the end point a sample thermally cycled 1500 times. Positron annihilation lifetime spectra and Coincidence Doppler Broadening profiles were obtained in various states and at various tem- peratures. It was found that the initial state was low in defects with positron lifetimes close to that of bulk NiTi. Cycling lead to a continuous build-up of a defect structure up to 20 0 −50 0 cycles after which saturation was reached. Two types of defects created during cycling were identified, namely pure dislo- cations and vacancies attached to dislocations.
Autor*innen: | M. LiuORCiD, P. Diercks, Anna Maria ManzoniORCiD, J. ČížekORCiD, U. RamamurtyORCiD, J. BanhartORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Acta Materialia |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
5 Werkstofftechnik / 5.2 Metallische Hochtemperaturwerkstoffe | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | Elsevier Ltd. |
Jahrgang/Band: | 220 |
Erste Seite: | 117298 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Austenite-to-martensite phase transformation; Defects; Positron annihilation spectroscopy; Shape memory alloy; Thermal Cycling |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.actamat.2021.117298 |
URN: | urn:nbn:de:kobv:b43-533641 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY - Namensnennung 4.0 International |
Datum der Freischaltung: | 27.09.2021 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 17.11.2021 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |