Surface water-induced broadening of crack initiation probability of zinc aluminosilicate glasses

  • The crack generation probability by Vickers indentation of glass surfaces is known to be influenced by the atmospheric conditions under which the Vickers experiment is performed [1]. However, the effect of surface water due to preparation and storage of the glass surfaces prior to the indentation is less understood. Therefore, zinc aluminosilicate glasses of perzinc, peraluminous as well as nominally NBO-free meta-aluminous composition were prepared by melt quenching. Surfaces of cut and polished specimens of these glasses were either stored for seven days under constant atmosphere (50 °C; 55% RH) or etched (HF: 20vol%; 20 min) shortly before indentation. The obtained results show a strong variation of crack initiation behavior depending on chemical composition of the glasses as well as sample preparation. All experiments were performed in dry nitrogen gas to minimize the influence of atmospheric humidity during indentation. While the regular glass surfaces exposed to humid air priorThe crack generation probability by Vickers indentation of glass surfaces is known to be influenced by the atmospheric conditions under which the Vickers experiment is performed [1]. However, the effect of surface water due to preparation and storage of the glass surfaces prior to the indentation is less understood. Therefore, zinc aluminosilicate glasses of perzinc, peraluminous as well as nominally NBO-free meta-aluminous composition were prepared by melt quenching. Surfaces of cut and polished specimens of these glasses were either stored for seven days under constant atmosphere (50 °C; 55% RH) or etched (HF: 20vol%; 20 min) shortly before indentation. The obtained results show a strong variation of crack initiation behavior depending on chemical composition of the glasses as well as sample preparation. All experiments were performed in dry nitrogen gas to minimize the influence of atmospheric humidity during indentation. While the regular glass surfaces exposed to humid air prior to Vickers indentation show a broad distribution of crack initiation probability, this distribution narrows down if etched glass surfaces are tested. SNMS depth profiling shows a water enriched layer at the surface (150 μm) for the non-etched and stored specimens leading to the conclusion that surface water causes broadening of the crack initiation probability of glass surfaces.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Vortrag_DGG_Weimar_Thorben_Welter.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:T. Welter
Koautor*innen:Marianne Nofz, Joachim Deubener
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Aluminosilicate glasses; Crack initiation probability; Surface water; Vickers indentation
Veranstaltung:91. Glastechnische Tagung
Veranstaltungsort:Weimar, Germany
Beginndatum der Veranstaltung:29.05.2017
Enddatum der Veranstaltung:31.05.2017
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:05.03.2018
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.