Sintering behavior, microstructure and thermoelectric properties of calcium cobaltite thickfilms for transversal thermoelectric multilayer generators

  • The sintering behavior and the thermoelectric performance of Ca3Co4O9 multilayer laminates were studied, and a multilayer thermoelectric generator was fabricated. Compacts and multilayer samples with anisotropic microstructure and residual porosity were obtained after conventional sintering at 920 °C, whereas dense and isotropic multilayer samples were prepared by firing at 1200 °C and reoxidation at 900 °C. A hot-pressed sample has a dense and anisotropic microstructure. Samples sintered at 920 °C exhibit low electrical conductivity due to the low density, whereas the Seebeck coefficient is not sensitive to preparation conditions. However, thermal conductivity of multilayers is very low, and, hence acceptable ZT values are obtained. A ransversal multilayer thermoelectric generator (TMLTEG) was fabricated by stacking layers of Ca3Co4O9 green tapes, AgPd conductor printing, and co-firing at 920 °C. The TMLTEG has a power output of 3 mW at ΔT =200 K in the temperature interval of 25 °CThe sintering behavior and the thermoelectric performance of Ca3Co4O9 multilayer laminates were studied, and a multilayer thermoelectric generator was fabricated. Compacts and multilayer samples with anisotropic microstructure and residual porosity were obtained after conventional sintering at 920 °C, whereas dense and isotropic multilayer samples were prepared by firing at 1200 °C and reoxidation at 900 °C. A hot-pressed sample has a dense and anisotropic microstructure. Samples sintered at 920 °C exhibit low electrical conductivity due to the low density, whereas the Seebeck coefficient is not sensitive to preparation conditions. However, thermal conductivity of multilayers is very low, and, hence acceptable ZT values are obtained. A ransversal multilayer thermoelectric generator (TMLTEG) was fabricated by stacking layers of Ca3Co4O9 green tapes, AgPd conductor printing, and co-firing at 920 °C. The TMLTEG has a power output of 3 mW at ΔT =200 K in the temperature interval of 25 °C to 300 °C.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Schulz_Toepfer_JECERS_2018.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:T. Schulz, T. Reimann, A. Bochmann, A. Vogel, B. Capraro, Björn MiellerORCiD, S. Teichert, J. Töpfer
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of the European Ceramic Society
Jahr der Erstveröffentlichung:2018
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.4 Multimateriale Fertigungsprozesse
Verlag:Elsevier Ltd.
Jahrgang/Band:38
Ausgabe/Heft:4
Erste Seite:1600
Letzte Seite:1607
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik
Freie Schlagwörter:Calcium cobaltite; Multilayer; Pressure-assisted sintering; Thermoelectric oxide
Themenfelder/Aktivitätsfelder der BAM:Energie
DOI:10.1016/j.jeurceramsoc.2017.11.017
ISSN:0955-2219
ISSN:1873-619X
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:31.01.2018
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:01.03.2018
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.