Degradation mechanism of short-fibre reinforced polyamide due to unaxial fatigue loading evaluated by non-destructive testing and fractography

  • The damage process of short glass fibre (30% weight) reinforced polyamide caused by mechanical loading was investigated from the beginning on micro cracking level to the incipient crack of mm-dimension. Based on high resolution computer tomography and the X-ray-refraction technique the inner surface due to micro-cracking at the short fibre ends and the fibre matrix debonding of the skin surface of the filament was determined quantitatively. With the knowledge of the fatigue crack propagation rate and fracture toughness of the material from former research projects, it was derived that the total inner surface due to micro cracks measured by X-ray refraction is much higher than the specimen could have withstand the load, supposed the surface is in a localized crack. Hence, the damage process could be described from micro to macro level. Accompanying fractographic investigations endorse the modelling based on the NDT-techniques.

Volltext Dateien herunterladen

  • ICFC2015-42-presentation.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Volker Trappe
Koautoren/innen:Stefan Günzel, Karoline Metzkes
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2015
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.0 Abteilungsleitung und andere
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Crack propagation; Damage evolution; Fractography; Fracture mechanics; PA-GF30; X-ray-refraction
Themenfelder/Aktivitätsfelder der BAM:Material
Veranstaltung:International Conference of Fatigue of Composites ICFC 6
Veranstaltungsort:Paris, France
Beginndatum der Veranstaltung:25.03.2015
Enddatum der Veranstaltung:27.03.2015
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:21.12.2016
Referierte Publikation:Nein