Experimental and analytical investigation of notched components of a Nickel based superalloy under high temperature cyclic loading
- While the increase in use of renewable energy sources is a necessity in times of climate change the use of gas turbines as back-up requires them to be run in a much more flexible manner in order to compensate for side effects like sudden fluctuations of energy generation. The significant changes of stress and temperature levels in turbine blades due to start-up and shut down can cause crack initiation and growth in the blades‘ alloy. The aim of this research project is to identify a model for lifetime prediction for gas turbine components made of a Nickel base superalloy under high temperature with a Focus on stress concentration points such as cooling holes.
Autor*innen: | Adam Butz |
---|---|
Koautor*innen: | Bernard FedelichORCiD, Birgit RehmerORCiD |
Dokumenttyp: | Posterpräsentation |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2017 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik | |
Freie Schlagwörter: | Gas turbine; LCF; Service life model |
Veranstaltung: | HIDA-7 Conference on Life/Crack Assessment & Failures in Industrial Structures, UK |
Veranstaltungsort: | Portsmouth, UK |
Beginndatum der Veranstaltung: | 15.05.2017 |
Enddatum der Veranstaltung: | 17.05.2017 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 04.10.2017 |
Referierte Publikation: | Nein |