Surface crystallization and gas bubble formation during conventional heat treatment in Na2MnP2O7 glass
- The crystallization behavior of sodium ion conductive Na2MnP2O7 glass was examined to clarify the crystallization mechanism. The formation of thermodynamically metastable phase, layered Na2MnP2O7, at the surface of the glass occurred. Heat treatment at 430 °C for 3 h lead to surface crystals of Na2MnP2O7 oriented with the (101) direction perpendicular to the sample surface. As the heat treatment temperature increased, the glass-ceramic samples deformed, and the presence numerous micro bubbles due to dissolved water was detected.
Autor*innen: | C. Akatsuka, T. Honma, Ralf Müller, Stefan ReinschORCiD, S. Tanaka, T. Komatsu |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Journal of Non-Crystalline Solids |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.6 Glas | |
Verlag: | Elsevier B.V. |
Jahrgang/Band: | 510 |
Erste Seite: | 36 |
Letzte Seite: | 41 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Bubble formation; Crystallization; Glass-ceramic; Phosphate; Sodium ion batteries |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.1016/j.jnoncrysol.2019.01.030 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 20.11.2019 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 20.11.2019 |