Experimental study on M23C6 nucleation and growth mechanisms in Ni-base superalloy single crystals

  • The addition of carbon to Ni-base superalloy single crystals has been increasingly carried out to improve low angle grain boundary (LAGB) resistance and castability. Consequently, the precipitation of carbides is highly probable during long-term application of components subjected to higher temperatures (> 1000 °C). While the view on the role of carbides as strengthening or detrimental is polemical, their inevitable increased presence in carbon-doped alloys must be addressed. In the present work, the evolution of M23C6 carbides forming in the commercial grade Ni-base superalloy LEK 94 during high-temperature and low-stress creep exposure is assessed. Although carbon is not intentionally added to the LEK 94 alloy, it admits up to 0.1 at. %, which together with the high content of M23C6-forming transition metals, leads to their precipitation. The precipitation is induced here during creep experiments at 1020 °C and a nominal applied stress of 160 MPa along [001]. The correlation ofThe addition of carbon to Ni-base superalloy single crystals has been increasingly carried out to improve low angle grain boundary (LAGB) resistance and castability. Consequently, the precipitation of carbides is highly probable during long-term application of components subjected to higher temperatures (> 1000 °C). While the view on the role of carbides as strengthening or detrimental is polemical, their inevitable increased presence in carbon-doped alloys must be addressed. In the present work, the evolution of M23C6 carbides forming in the commercial grade Ni-base superalloy LEK 94 during high-temperature and low-stress creep exposure is assessed. Although carbon is not intentionally added to the LEK 94 alloy, it admits up to 0.1 at. %, which together with the high content of M23C6-forming transition metals, leads to their precipitation. The precipitation is induced here during creep experiments at 1020 °C and a nominal applied stress of 160 MPa along [001]. The correlation of precipitation and external load is carried out by evaluating the carbides in the gage section of parallel and circularly notched cylindrical samples, as well as in their heads. Characterization is made by transmission electron microscopy (TEM). Although primary MC carbides form mostly in interdendritic regions during casting, high temperature exposure induces M23C6 carbide nucleation especially in the γ phase of dendritic regions, where a stronger partitioning of refractory elements is present. The carbides have a needle shape with their main axis on 〈100〉 and a cube-on-cube orientation relationship. They present incoherent {100} facets along their elongated region and semi-coherent {111} facets at their ends. Their nucleation and growth mechanisms are discussed based on microstructural observation under different experimental conditions.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Agudo 2017 Model and Simul of Superal Poster_A3.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Leonardo Agudo JácomeORCiD
Dokumenttyp:Posterpräsentation
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Carbide; Creep; Ni-base superalloy; Scanning transmission electron microscopy (STEM); Single cystal
Veranstaltung:Modelling and Simulation of Superalloys. International Workshop.
Veranstaltungsort:Bochum, Germany
Beginndatum der Veranstaltung:29.03.2017
Enddatum der Veranstaltung:31.03.2017
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:15.05.2017
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.