Immobilization of photocatalytically active TiO2 nanopowder by high shear granulation

  • Nano-TiO2 powder is known to show high photocatalytic reactivity in the degradation of several organic pollutants. In thiswork, the powderwas fixed on the surface of SiO2 granuleswith the size of several micrometers using a high shear granulation process. Nanozirconia sol was applied as an inorganic binder. When the samples were tempered at 300 °C, they showed high stability in an aqueous solution for several hours. An energy dispersive x-ray spectroscopy (EDX) analysis confirmed that the cores and shells of the granules consisted solely of SiO2 and TiO2 respectively, and that ZrO2 was found throughout the whole granules. Methylene blue (MB) was employed as amodel systemto evaluate the photocatalytic activity of the TiO2 nanopowder and coated granules. Itwas shown that the TiO2-coated granules lead to the degradation ofMB under UV irradiation,whereas no effect was observed in the dark. After the Degradation experiments the granules could be recovered and they remained active forNano-TiO2 powder is known to show high photocatalytic reactivity in the degradation of several organic pollutants. In thiswork, the powderwas fixed on the surface of SiO2 granuleswith the size of several micrometers using a high shear granulation process. Nanozirconia sol was applied as an inorganic binder. When the samples were tempered at 300 °C, they showed high stability in an aqueous solution for several hours. An energy dispersive x-ray spectroscopy (EDX) analysis confirmed that the cores and shells of the granules consisted solely of SiO2 and TiO2 respectively, and that ZrO2 was found throughout the whole granules. Methylene blue (MB) was employed as amodel systemto evaluate the photocatalytic activity of the TiO2 nanopowder and coated granules. Itwas shown that the TiO2-coated granules lead to the degradation ofMB under UV irradiation,whereas no effect was observed in the dark. After the Degradation experiments the granules could be recovered and they remained active for further applications.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Goedecke_Powder_Technology.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Caroline Goedecke, Regine Sojref, Thi Yen Nguyen, Christian Piechotta
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Powder Technology
Jahr der Erstveröffentlichung:2017
Jahrgang/Band:318
Erste Seite:465
Letzte Seite:470
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Sanitär- und Kommunaltechnik; Umwelttechnik
Freie Schlagwörter:Advanced oxidation; Heterogeneous photocatalysis; Methylene blue; Nanozirconia; Water treatment
DOI:10.1016/j.powtec.2017.06.025
ISSN:0032-5910
ISSN:1873-328X
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:25.08.2017
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:25.08.2017
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.