Comparative study on high temperature oxidation of T92 steel in dry and wet oxyfuel environments

  • Fireside oxidation of T92 steel was studied after exposure times up to 1000 h in the temperature range of 580–650 °C in simulated dry (CO2–27 % N2–2 % O2–1 % SO2) and wet (CO2–20 % H2O–7 % N2–2 % O2–1 % SO2) oxyfuel environments. Water vapour addition to the oxyfuel gas substantially increased the oxidation rate. The oxide scales developed under wet environment contained more defects, resulting in higher access of oxidants to the substrate material and enhanced oxidation. In addition, the oxide scales had lower chromium enrichment in the inner layer as compared to that in the dry condition. The oxide scales consisted of hematite and magnetite in the outer layer and a mixture of (Fe, Cr)-spinel, sulphides and wustite in the inner layer. The sulphur distribution differed between the oxide scales developed in dry and wet oxyfuel environments. Sulphur was mainly concentrated in the inner layer and at the oxide/alloy interface. In contrast to the wet oxyfuel gas, very high sulphurFireside oxidation of T92 steel was studied after exposure times up to 1000 h in the temperature range of 580–650 °C in simulated dry (CO2–27 % N2–2 % O2–1 % SO2) and wet (CO2–20 % H2O–7 % N2–2 % O2–1 % SO2) oxyfuel environments. Water vapour addition to the oxyfuel gas substantially increased the oxidation rate. The oxide scales developed under wet environment contained more defects, resulting in higher access of oxidants to the substrate material and enhanced oxidation. In addition, the oxide scales had lower chromium enrichment in the inner layer as compared to that in the dry condition. The oxide scales consisted of hematite and magnetite in the outer layer and a mixture of (Fe, Cr)-spinel, sulphides and wustite in the inner layer. The sulphur distribution differed between the oxide scales developed in dry and wet oxyfuel environments. Sulphur was mainly concentrated in the inner layer and at the oxide/alloy interface. In contrast to the wet oxyfuel gas, very high sulphur concentration was measured in the inner oxide scale formed in the dry oxyfuel gas. Additionally, Fe-sulphide was formed at the interface of inner and outer oxide layer in the wet condition.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 10.1007_s11085-015-9565-0.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Kamlesh Chandra, Axel KranzmannORCiD, Romeo Saliwan Neumann, F. Rizzo
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Oxidation of metals
Jahr der Erstveröffentlichung:2015
Verlag:Springer
Verlagsort:New York, NY
Jahrgang/Band:84
Ausgabe/Heft:3-4
Erste Seite:463
Letzte Seite:490
Freie Schlagwörter:High temperature corrosion; Oxidation; Oxyfuel environment; Sulphur; Water vapour
DOI:10.1007/s11085-015-9565-0
ISSN:0030-770X
ISSN:1573-4889
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:19.10.2015
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.