A Study on antioxidant depletion and degradation in polyolefin based geosynthetics: sacrificial versus regenerative stabilization

  • Plastic products used in geotechnical engineering, so-called geosynthetics, are often made of polyolefins (polyethylene or polypropylene) and stabilized against oxidative degradation by antioxidants (AO). Three types of AO “packages” are used: (P1) phenols and phosphites/sulfides, (P2) hindered amines (HAS) with a marginal stabilization P1 of the basic resin, (P3) a combination of packages P1 and P2 with comparable amounts of phenol and HAS. We report about long-lasting oven aging and water immersion tests at 80 °C of 29 different polyolefin based products (geomembranes, geonets and geotextiles). Pronounced differences in the degradation behavior were found depending solely on the type of AO package. In case of P1, the oxidative degradation is prevented by the AO. Autocatalytic oxidation only begins after depletion of AO and may lead to catastrophic failure depending on the environmental conditions. In case of P2, degradation starts right from the beginning. However, it is deceleratedPlastic products used in geotechnical engineering, so-called geosynthetics, are often made of polyolefins (polyethylene or polypropylene) and stabilized against oxidative degradation by antioxidants (AO). Three types of AO “packages” are used: (P1) phenols and phosphites/sulfides, (P2) hindered amines (HAS) with a marginal stabilization P1 of the basic resin, (P3) a combination of packages P1 and P2 with comparable amounts of phenol and HAS. We report about long-lasting oven aging and water immersion tests at 80 °C of 29 different polyolefin based products (geomembranes, geonets and geotextiles). Pronounced differences in the degradation behavior were found depending solely on the type of AO package. In case of P1, the oxidative degradation is prevented by the AO. Autocatalytic oxidation only begins after depletion of AO and may lead to catastrophic failure depending on the environmental conditions. In case of P2, degradation starts right from the beginning. However, it is decelerated and proceeds gradually. In case of P3, the degradation behavior seems to be a superposition of the characteristics obtained for P1 and P2. Plotting the fractional loss of the AO in P1 and P2 as function of the square root of aging time, we identified two regimes of AO depletion. We suggest to attribute this observation to the different mechanisms of AO depletion.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Müller et al 2016.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Werner Müller, Ines Jakob, Renate Tatzky-Gerth, Andreas Wöhlecke
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer engineering and science
Jahr der Erstveröffentlichung:2016
Herausgeber (Institution):Society of plastics engineers
Verlag:John Wiley & Sons
Verlagsort:New York
Jahrgang/Band:56
Ausgabe/Heft:2
Erste Seite:129
Letzte Seite:142
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Antioxidant; Geosynthetics; Oxidation; Stabilization
DOI:10.1002/pen.24199
ISSN:0032-3888
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:29.03.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:20.04.2016
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.