Cohesive Zone Modelling Approach on Irradiated Claddings Subjected to Long-Term Dry Interim Storage

  • Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. Pre-storage drying and the early stage of interim storage can subject the cladding to higher temperatures and higher pressure induced tensile hoop stresses than those associated with in-reactor operation and pool storage. Under these conditions, radial hydrides may precipitate in zirconium-based alloys (Zircaloy) during slow cooling, which may result in embrittlement of the cladding material and eventually a sudden failure of cladding under additional mechanical loads. Especially long, continuous radial hydride structures and low temperature can cause severe embrittlement of claddings and finally failure by fracture even at small deformations. The focus of the presented research is on the development of appropriate numerical methods for predicting the mechanical behaviour and identification of limitingLong-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. Pre-storage drying and the early stage of interim storage can subject the cladding to higher temperatures and higher pressure induced tensile hoop stresses than those associated with in-reactor operation and pool storage. Under these conditions, radial hydrides may precipitate in zirconium-based alloys (Zircaloy) during slow cooling, which may result in embrittlement of the cladding material and eventually a sudden failure of cladding under additional mechanical loads. Especially long, continuous radial hydride structures and low temperature can cause severe embrittlement of claddings and finally failure by fracture even at small deformations. The focus of the presented research is on the development of appropriate numerical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. An iterative inverse analysis method is used for deriving the elastic-plastic material properties in the hoop direction of a ring-shaped sample. A modelling approach based on cohesive zones is explained which can reproduce the propagation of cracks initiated at radial hydrides in the zirconium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hydrides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 230526_BAM_SEDS23.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Mohan Reddy Gaddampally
Koautor*innen:Uwe Zencker, Holger Völzke
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2023
Organisationseinheit der BAM:3 Gefahrgutumschließungen; Energiespeicher
3 Gefahrgutumschließungen; Energiespeicher / 3.4 Sicherheit von Lagerbehältern
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik
Freie Schlagwörter:Ageing Management; Cladding Embrittlement; Extended Storage; Ring Compression Test; Spent Nuclear Fuel
Themenfelder/Aktivitätsfelder der BAM:Energie
Energie / Kerntechnische Entsorgung
Veranstaltung:7th GRS Workshop on the Safety of Extended Dry Storage of Spent Nuclear Fuel
Veranstaltungsort:Garching, Germany
Beginndatum der Veranstaltung:24.05.2023
Enddatum der Veranstaltung:26.05.2023
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:13.10.2023
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.