Study on Phase Separation of PET/PEN Blends by Dynamic Rheology

  • Blends of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalate) (PEN) were processed into biaxially drawn films, and samples taken from the bi-oriented films were then investigated by dynamic rheology experiments in the melt state. Storage modulus G and loss modulus G were determined in the frequency range of 10-2-102 rad/s at temperatures between 260 and 300°C. Although the time-temperature superposition (TTS) principle was found to hold in the high frequency regime, a breakdown of TTS was observed at low frequencies, and the terminal behavior of the storage modulus G of the blends departs drastically from the terminal behavior observed for the blend components. This is caused by interfacial surface tension effects. The results indicate that despite the effect of transesterification reactions, the PET/PEN blend systems investigated consist of a microseparate phase of PEN platelets in a matrix of PET. This morphology is produced when the blends are processed into biaxiallyBlends of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalate) (PEN) were processed into biaxially drawn films, and samples taken from the bi-oriented films were then investigated by dynamic rheology experiments in the melt state. Storage modulus G and loss modulus G were determined in the frequency range of 10-2-102 rad/s at temperatures between 260 and 300°C. Although the time-temperature superposition (TTS) principle was found to hold in the high frequency regime, a breakdown of TTS was observed at low frequencies, and the terminal behavior of the storage modulus G of the blends departs drastically from the terminal behavior observed for the blend components. This is caused by interfacial surface tension effects. The results indicate that despite the effect of transesterification reactions, the PET/PEN blend systems investigated consist of a microseparate phase of PEN platelets in a matrix of PET. This morphology is produced when the blends are processed into biaxially oriented PET/PEN films, and droplets of PEN are deformed into a lamellar structure consisting of parallel and extended, separate layers. The large interfacial surface area of the bi-oriented PET/PEN blends leads to remarkably strong interfacial tension effects in dynamic rheology measurements.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:M.H. Wagner, W. Wu, Y. Liu, Q. Qian, Y. Zhang, Werner Mielke
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of applied polymer science
Jahr der Erstveröffentlichung:2008
Verlag:Wiley InterScience
Verlagsort:Hoboken, NJ
Jahrgang/Band:110
Ausgabe/Heft:1
Erste Seite:177
Letzte Seite:182
Freie Schlagwörter:Bi-oriented films; Dynamic rheology; PET/PEN blends; Phase separation; Surface tension; Time-temperature superposition
DOI:10.1002/app.28156
ISSN:0021-8995
ISSN:1097-4628
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:08.09.2008
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.