Carbon-fibre epoxy prepreg (CFC) curing in an autoclave analogue process controlled by dynamic mechanical analysis (DMA)

  • Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.

Volltext Dateien herunterladen

  • 1-s2.0-S0142941813001979-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Wolfgang Stark, Matthias Jaunich, J. McHugh
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer Testing
Jahr der Erstveröffentlichung:2013
Organisationseinheit der BAM:3 Gefahrgutumschließungen
3 Gefahrgutumschließungen / 3.4 Sicherheit von Lagerbehältern
Verlag:Elsevier Science
Verlagsort:Amsterdam [u.a.]
Jahrgang/Band:32
Ausgabe/Heft:8
Erste Seite:1487
Letzte Seite:1494
Freie Schlagwörter:Autoclave; CFC; Curing; DMA; DSC; Gelation; Glass transition; Prepreg; Vitrification
DOI:https://doi.org/10.1016/j.polymertesting.2013.09.014
ISSN:0142-9418
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:11.11.2013