Determination and interpretation of changes in thermophysical properties of a carbon-fibre prepreg during cure

  • Epoxy composites used for high-end structural applications are typically cured under the influence of temperature and pressure causing a number of complex chemical and physical transformations. On heating a mould, temperature gradients will occur through the component which will depend largely on the thermophysical properties of the specific composite. The crosslinking reaction is exothermic leading to additional heat release, thus complicating heat transportation models. If such effects are not accounted for, it can lead to variations in resin flow, poor fibre wetting causing voiding and inhomogeneous cure, leading to shrinkage and unfavourable variations in moulded part geometry. Limited information is available for thermal models used in the manufacture of reinforced thermosets. Autoclave [1, 2] and laser or infra-red curing processes [3, 4] typically use constant values determined on fully cured parts. In this work, the variation in thermal conductivity (K) (W/(m K)), thermalEpoxy composites used for high-end structural applications are typically cured under the influence of temperature and pressure causing a number of complex chemical and physical transformations. On heating a mould, temperature gradients will occur through the component which will depend largely on the thermophysical properties of the specific composite. The crosslinking reaction is exothermic leading to additional heat release, thus complicating heat transportation models. If such effects are not accounted for, it can lead to variations in resin flow, poor fibre wetting causing voiding and inhomogeneous cure, leading to shrinkage and unfavourable variations in moulded part geometry. Limited information is available for thermal models used in the manufacture of reinforced thermosets. Autoclave [1, 2] and laser or infra-red curing processes [3, 4] typically use constant values determined on fully cured parts. In this work, the variation in thermal conductivity (K) (W/(m K)), thermal diffusivity (a) (m(2)/s) and specific heat capacity at constant pressure (c(p)) (J/(g K) is determined for a carbon fibre prepreg during cure. It is the intention to improve understanding of how these parameters are related to chemical or physical transformations occurring during cure, and where estimates or shortcuts may be used for heat transfer modelszeige mehrzeige weniger

Volltext Dateien herunterladen

  • McHugh_Determination and interpretation.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Jarlath McHugh, Wolfgang Stark
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer Testing
Jahr der Erstveröffentlichung:2016
Verlag:Elsevier Science
Verlagsort:Oxford
Jahrgang/Band:49
Erste Seite:115
Letzte Seite:120
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Differential scanning calorimetry; Epoxy system; Temerature
DOI:10.1016/j.polymertesting.2015.11.015
ISSN:0142-9418
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.04.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:20.04.2016
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.