Biaxial path-dependence of low-cycle fatigue behaviour and microstructure of alloy 800 H at room temperature

  • Low-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed inLow-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed in the specimens after proportional and nonproportional LCF tests.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Feng Jiao, Werner ÖsterleORCiD, Pedro Dolabella PortellaORCiD, Josef Ziebs
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Materials science and engineering A
Jahr der Erstveröffentlichung:1995
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:196
Ausgabe/Heft:1
Erste Seite:19
Letzte Seite:24
DOI:10.1016/0921-5093(94)09690-2
ISSN:0921-5093
ISSN:1873-4936
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:ZM 26A
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:16.05.2003
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.