“Cube slip” in near-[111] oriented specimens of a single-crystal nickel-base superalloy

  • In the past few years, it has been discussed with increasing frequency, whether cube slip does occur in gamma' hardened nickel-base superalloys. Occurrence of cube slip has consequences for the modeling of orientation dependence of the CRSS. Until now, there are only few experimental investigations. In principle, cube slip should be possible in primitive cubic lattices (e.g. L12 ordered gamma' phase) but not in face centered cubic ones (e.g. Ni solid solution). The most favourable specimen orientations are near [111], where the Schmid factors for this type of glide exceed those for octahedral systems. There are two basic methods to detect cube slip: macroscopic slip trace analysis and Transmission electron microscopy (TEM) investigation of the dislocation structure. Few observations of cube slip by macroscopic slip traces are reported in the literature. But it is still uncertain under which test conditions cube slip occurs and what the dislocation mechanisms are. Cube slip wasIn the past few years, it has been discussed with increasing frequency, whether cube slip does occur in gamma' hardened nickel-base superalloys. Occurrence of cube slip has consequences for the modeling of orientation dependence of the CRSS. Until now, there are only few experimental investigations. In principle, cube slip should be possible in primitive cubic lattices (e.g. L12 ordered gamma' phase) but not in face centered cubic ones (e.g. Ni solid solution). The most favourable specimen orientations are near [111], where the Schmid factors for this type of glide exceed those for octahedral systems. There are two basic methods to detect cube slip: macroscopic slip trace analysis and Transmission electron microscopy (TEM) investigation of the dislocation structure. Few observations of cube slip by macroscopic slip traces are reported in the literature. But it is still uncertain under which test conditions cube slip occurs and what the dislocation mechanisms are. Cube slip was observed during tensile or compression tests of several first generation superalloys, but it seems not to occur during shear creep deformation (e.g. CMSX-4 at 980°C), and it is also lacking under conventional tensile or compression loading, if the gmma' particles are small. No observations were ever reported of dislocations gliding on {001} planes in matrix channels.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 1999-Bettge-Oesterle-Cube-Slip-Scripta-Mat.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Dirk BettgeORCiD, Werner ÖsterleORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Scripta Materialia
Jahr der Erstveröffentlichung:1999
Verlag:Elsevier
Jahrgang/Band:40
Ausgabe/Heft:4
Erste Seite:389
Letzte Seite:395
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Cube slip; Dislocations; Nickel-base superalloy; TEM
DOI:10.1016/S1359-6462(98)00446-1
ISSN:1359-6462
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:14.11.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.