Biaxial path-dependence of low-cycle fatigue behaviour and microstructure of alloy 800 H at room temperature
- Low-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed inLow-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed in the specimens after proportional and nonproportional LCF tests.…
Autor*innen: | Feng Jiao, Werner ÖsterleORCiD, Pedro Dolabella PortellaORCiD, Josef Ziebs |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Materials science and engineering A |
Jahr der Erstveröffentlichung: | 1995 |
Verlag: | Elsevier |
Verlagsort: | Amsterdam |
Jahrgang/Band: | 196 |
Ausgabe/Heft: | 1 |
Erste Seite: | 19 |
Letzte Seite: | 24 |
DOI: | 10.1016/0921-5093(94)09690-2 |
ISSN: | 0921-5093 |
ISSN: | 1873-4936 |
Verfügbarkeit des Dokuments: | Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access") |
Bibliotheksstandort: | ZM 26A |
Datum der Freischaltung: | 19.02.2016 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 16.05.2003 |