Fracture mechanics based assessment of the fatigue strength: approach for the determination of the initial crack size

  • In a number of previous papers, the authors have proposed a model for fracture mechanics based prediction of the S-N characteristics of metallic components with large microstructural defects. Here, an extension to materials that do not show large defects onto the fracture surfaces is provided. In such cases, an approach based on a so-called cyclic R-curve analysis is proposed for the determination of the initial flaw size, which has to be used in the calculation of fatigue crack propagation. The principle is explained and demonstrated by a first application to a welded joint.

Volltext Dateien herunterladen

  • Zerbst_et_al-2015-Fatigue_-_Fracture_of_Engineering_Materials_.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Uwe Zerbst, Mauro Madia
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Fatigue & fracture of engineering materials & structures
Jahr der Erstveröffentlichung:2015
Verlag:Blackwell
Verlagsort:Oxford
Jahrgang/Band:38
Ausgabe/Heft:9
Erste Seite:1066
Letzte Seite:1075
Freie Schlagwörter:Cyclic R-curve; Fatigue strength; Initial flaw size; Short cracks; Weldments
DOI:10.1111/ffe.12288
ISSN:1460-2695
ISSN:0160-4112
ISSN:8756-758X
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.