Material defects as cause for the fatigue failure of metallic components
- The paper provides an overview on material defects which may serve as fatigue crack initiation sites and can cause final fatigue failure of a component. These comprise nonmetallic inclusions in Steel and aluminum alloys, cavities such as pores, micro-shrinkages and un-welded regions in cast, sinter and additively manufactured alloys, graphite nodules, shrinkages and other items in modular cast iron, regions of defective microstructure, microcracks and secondary notches such as undercuts and surface roughness. Besides their origin, the effect and mechanisms on fatigue crack initiation and propagation are discussed. The considerations are proceeded and accompanied by a Brief discussion of some Basic aspects such as the stages of crack propagation along their length scale, the overcoming of crack arrest and the question when a secondary notch can be treated as a crack.
Autor*innen: | Uwe Zerbst, Christian Klinger |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | International Journal of Fatigue |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
Verlag: | Elsevier |
Jahrgang/Band: | 127 |
Erste Seite: | 312 |
Letzte Seite: | 323 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Fatigue strength and life; Graphite modules; Material defects; Non-metallic inclusions; Pores; Shrinkages; Surface roughness |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.ijfatigue.2019.06.024 |
ISSN: | 0142-1123 |
ISSN: | 1879-3452 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 27.09.2019 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 27.09.2019 |