- If a component is cyclically loaded, its load carrying capacity is considerably lower than in the monotonic loading case. This general observation applies in particular to L-PBF parts. The causes of this are mainly material defects such as pores and unwelded regions (Chapter 8) and a pronounced surface roughness in the as-built condition (Chapter 9). In addition, effects due to the anisotropy of the microstructure (Chapter 6) and a complex residual stress pattern (Chapter 7) play an important role. A consequence is that common strategies of fatigue assessment cannot be transferred to L-PBF applications without modifications. Due to the inhomogeneity of the material, the determination of representative material properties and the transfer to the component is a problem, and this is also the case with regard to the consideration of defects, surface roughness and residual stresses. The chapter gives a brief introduction to these problem areas.
Autor*innen: | Uwe Zerbst, Mauro Madia |
---|---|
Persönliche Herausgeber*innen: | I. Yadroitsev, I. Yadroitsava, A. Du Plessies, E. McDonald |
Dokumenttyp: | Buchkapitel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Fundamentals of laser powder bed fusion of metals |
Auflage: | 1 |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
Verlag: | Elsevier Inc. |
Verlagsort: | Amsterdam |
Erste Seite: | 377 |
Letzte Seite: | 394 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Fatigue crack propagation stagesdefects; Fatigue life; Fatigue strength; Fracture mechanics |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Additive Fertigung | |
Material / Degradation von Werkstoffen | |
DOI: | 10.1016/B978-0-12-824090-8.00015-9 |
ISBN: | 978-0-12-824090-8 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 24.06.2021 |
Referierte Publikation: | Nein |