Determination of fatigue crack propagation thresholds for steel in presence of environmental effects
- The experimental determination of the resistance to fatigue crack propagation in steel, particularly in the socalled near-threshold regime, is a crucial issue for safety-relevant components which are designed to operate for a large number of loading cycles before undergoing periodic inspections. This work summarizes the most relevant results of extensive experimental campaigns conducted at BAM and IPM over the last years, which have been devoted to the determination of fatigue crack propagation characteristics on medium and high strength steels. The influence of environment, oxide-induced crack closure and test methodologies in the near-threshold regime are discussed.
Autor*innen: | Mauro Madia, T. Vojtek, Larissa DuarteORCiD, Uwe Zerbst, P. Pokorný, M. Jambor, P. Hutař |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | International Journal of Fatigue |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
Verlag: | Elsevier Ltd. |
Jahrgang/Band: | 153 |
Aufsatznummer: | 106449 |
Erste Seite: | 1 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Environmental effect Fatigue crack propagation threshold; Oxide-induced crack closure; Steel |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.1016/j.ijfatigue.2021.106449 |
ISSN: | 0142-1123 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 14.10.2021 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 14.10.2021 |