Weathering resistance of halogen-free flame retardance in thermoplastics
- The influence of weathering on the fire retardancy of polymers is investigated by means of a cone calorimeter test, before and after artificial weathering. The surface degradation was monitored using different techniques (ATR–FTIR, microscopy, colour measurement). Different kinds of polymeric materials were chosen, all as they are used in practice: polycarbonate (PC) blends, polyamide (PA) and polypropylene (PP) flame-retarded with arylphosphate, melamine cyanurate (MC) and intumescent formulation based on ammonium polyphosphate (APP), respectively.
All samples show material degradation at the surface due to weathering. No significant weathering influence occurs on the flame retardancy when it is a bulk property, as was observed for aryl phosphates in PC blends and MC in PA. When the fire retardancy is dominated by a surface mechanism, dependence on the duration of weathering is detected: for intumescent formulations based on ammonium APP in PP, a worsening in the formation of theThe influence of weathering on the fire retardancy of polymers is investigated by means of a cone calorimeter test, before and after artificial weathering. The surface degradation was monitored using different techniques (ATR–FTIR, microscopy, colour measurement). Different kinds of polymeric materials were chosen, all as they are used in practice: polycarbonate (PC) blends, polyamide (PA) and polypropylene (PP) flame-retarded with arylphosphate, melamine cyanurate (MC) and intumescent formulation based on ammonium polyphosphate (APP), respectively.
All samples show material degradation at the surface due to weathering. No significant weathering influence occurs on the flame retardancy when it is a bulk property, as was observed for aryl phosphates in PC blends and MC in PA. When the fire retardancy is dominated by a surface mechanism, dependence on the duration of weathering is detected: for intumescent formulations based on ammonium APP in PP, a worsening in the formation of the intumescent network was observed.…
Autor*innen: | Ulrike BraunORCiD, Volker WachtendorfORCiD, Anja Geburtig, Horst Bahr, Bernhard SchartelORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Polymer degradation and stability |
Jahr der Erstveröffentlichung: | 2010 |
Verlag: | Applied Science Publ. |
Verlagsort: | London |
Jahrgang/Band: | 95 |
Ausgabe/Heft: | 12 |
Erste Seite: | 2421 |
Letzte Seite: | 2429 |
Freie Schlagwörter: | Cone calorimeter; Degradation; Fire retardancy; Intumescence; Weathering resistance |
DOI: | 10.1016/j.polymdegradstab.2010.08.020 |
ISSN: | 0141-3910 |
ISSN: | 1873-2321 |
Verfügbarkeit des Dokuments: | Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access") |
Bibliotheksstandort: | Sonderstandort: Publica-Schrank |
Datum der Freischaltung: | 19.02.2016 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 02.12.2010 |