Different aspects of the accelerated oxidation of polypropylene at increased pressure in an autoclave with regard to temperature, pretreatment and exposure media

  • The aim of this study is to investigate and compare three different factors, temperature, pretreatment and exposure media, on the oxidation and aging behavior of polypropylene (PP) bulk samples in the autoclave test under increased oxygen pressure. The aging of polypropylene, in this case syringe material, was accelerated under different conditions. The samples were aged at 75°, 80° and 85 °C under pure oxygen and at 75 °C under ultrapure water. Further samples treated with 15 kGy (e-beam) were aged at 75 °C under pure oxygen. All experiments were carried out at an oxygen partial pressure of 50 bar. The different courses of aging were evaluated and compared. Color and transparency were used to assess the visual changes; weight, geometry and tensile test for the changes in technical properties; and DSC, FTIR and TDS-GC-MS to improve our physico-chemical understanding of the aging processes. The investigations showed that all factors tested influence oxidation/aging behaviour. Dry orThe aim of this study is to investigate and compare three different factors, temperature, pretreatment and exposure media, on the oxidation and aging behavior of polypropylene (PP) bulk samples in the autoclave test under increased oxygen pressure. The aging of polypropylene, in this case syringe material, was accelerated under different conditions. The samples were aged at 75°, 80° and 85 °C under pure oxygen and at 75 °C under ultrapure water. Further samples treated with 15 kGy (e-beam) were aged at 75 °C under pure oxygen. All experiments were carried out at an oxygen partial pressure of 50 bar. The different courses of aging were evaluated and compared. Color and transparency were used to assess the visual changes; weight, geometry and tensile test for the changes in technical properties; and DSC, FTIR and TDS-GC-MS to improve our physico-chemical understanding of the aging processes. The investigations showed that all factors tested influence oxidation/aging behaviour. Dry or wet exposure has no effect on aging during the induction time. However, after the point of maximum service time the degradation process of polymer changes significantly in the presence of water. The increase of aging temperature decreases the maximum service time; however a temperature higher than 80 °C changes the relative ratio of surface and bulk oxidation. The pretreatment with irradiation decreases the maximum service time further, because the irradiation partly damages the antioxidant, and the mobility of antioxidant fragments inside the polymer changes. These diffusion effects influence the relative ratio of bulk and surface oxidation of the polymer sample.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 1-s2.0-S0142941814001147-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Kamila Bajer, Ulrike BraunORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer testing
Jahr der Erstveröffentlichung:2014
Verlag:Elsevier Science
Verlagsort:Amsterdam [u.a.]
Jahrgang/Band:37
Erste Seite:102
Letzte Seite:111
Freie Schlagwörter:Accelerated aging; Autoclave test; Electron radiation; Polypropylene
DOI:10.1016/j.polymertesting.2014.05.006
ISSN:0142-9418
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:19.06.2014
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.