Humidity resistant MoS2 coatings deposited by unbalanced magnetron sputtering

  • MoS2 is a suitable solid lubricant for environments free of oxygen or water vapor (i.e. vacuum). Humid air degrades film properties due to oxidation accompanied by high wear and increasing coefficients of friction. The present study aims at the further development of sputtered pure MoS2 coatings, extending their applicability to varying environmental conditions by increasing the resistance against humidity. The systematic coating development process is supported by using an experimental Box–Behnken design with variations of the deposition parameters cathode voltage, target/substrate distance, temperature and argon gas pressure. In contrast to common one-factor-at-a-time (OFAT) studies, this approach enables a determination of interactions between deposition process parameters and tribological–mechanical MoS2 film properties. The tribological improvement focuses on a maximization of wear resistance in air and vacuum measured in ball-on-disk experiments. The evaluated mechanicalMoS2 is a suitable solid lubricant for environments free of oxygen or water vapor (i.e. vacuum). Humid air degrades film properties due to oxidation accompanied by high wear and increasing coefficients of friction. The present study aims at the further development of sputtered pure MoS2 coatings, extending their applicability to varying environmental conditions by increasing the resistance against humidity. The systematic coating development process is supported by using an experimental Box–Behnken design with variations of the deposition parameters cathode voltage, target/substrate distance, temperature and argon gas pressure. In contrast to common one-factor-at-a-time (OFAT) studies, this approach enables a determination of interactions between deposition process parameters and tribological–mechanical MoS2 film properties. The tribological improvement focuses on a maximization of wear resistance in air and vacuum measured in ball-on-disk experiments. The evaluated mechanical properties are hardness, elastic modulus and residual stresses. These stresses were determined by the substrate curvature method. The study reveals that the residual stress state in the films and the hardness-to-modulus ratio are crucial for their tribological performance in humid air and vacuum environments. After a detailed determination of the relationships between deposition conditions and film properties, some selected microstructural analyses are presented which show that a substantially basal orientation of the lattice has positive effects on wear but also causes anisotropic film properties which result in fissile fracture of the coating if strong shock or point loads occur.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 1-s2.0-S0257897213006762-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:B. Vierneusel, Thomas Schneider, S. Tremmel, S. Wartzack, Thomas GradtORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Surface and coatings technology
Jahr der Erstveröffentlichung:2013
Verlag:Elsevier B.V.
Jahrgang/Band:235
Erste Seite:97
Letzte Seite:107
Freie Schlagwörter:Humidity resistance; MoS2; Residual stress; Unbalanced magnetron sputtering
DOI:10.1016/j.surfcoat.2013.07.019
ISSN:0257-8972
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:11.12.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.