Critical conditions for weld solidification crack growth

  • The occurrence of solidification cracking during welding remains a little understood phenomenon, in spite of extensive studies and tests performed to evaluate and compare the relative weldability of many different alloys. From an approach often adopted in the welding community attributed to Prokhorov, solidification cracks are believed to form when a critical tensile strain is exceeded, specific to the alloy, assuming that the mushy-zone has limited ductility. Tensile stresses and strains normally form behind a moving weld pool as a result of solidification shrinkage and thermal contraction, as influenced by welding parameters and the degree of restraint.

Volltext Dateien herunterladen

  • 9783642168635-c1.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Carl Edward Cross, Nicolas Coniglio, Philipp Schempp, M.G. Mousavi
Persönliche Herausgeber*innen:J. Lippold, T. Böllinghaus, C.E. Cross, et al.
Dokumenttyp:Beitrag zu einem Sammelband
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Hot cracking phenomena in welds III
Jahr der Erstveröffentlichung:2011
Verlag:Springer
Verlagsort:Berlin, Heidelberg
Ausgabe/Heft:Part 2
Erste Seite:25
Letzte Seite:41
Freie Schlagwörter:Aluminium alloy; Crack growth; Solidification cracking; Strain rate model
DOI:10.1007/978-3-642-16864-2_2
ISBN:978-3-642-16863-5
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.