Flame retardancy mechanisms of aryl phosphates in combination with boehmite in bisphenol A polycarbonate/acrylonitrile-butadiene-styrene blends

  • The influence of nano-dispersed 5 wt.% boehmite (AlOOH) and 5 wt.% AlOOH combined with bisphenol A bis(diphenyl phosphate) (BDP) in bisphenol A polycarbonate/acrylonitrile–butadiene–styrene (PC/ABS) + poly(tetrafluoroethylene) (PTFE), and 1 wt.% AlOOH with and without BDP, resorcinol bis(diphenyl phosphate) (RDP), and triphenyl phosphate (TPP), on PC/ABS + PTFE has been investigated. Possible flame retardancy mechanisms are revealed. Thermogravimetry (TG) and evolved gas analysis (TG-FTIR) are used to study pyrolysis, a cone calorimeter applying different external heat fluxes is used to investigate fire behaviour, and LOI and UL 94 are used to investigate flammability. Fire residues were investigated using ATR-FTIR. Adding 5 wt.% AlOOH decreases the peak heat release rate, as also has been reported for polymer nanocomposites with other layered structures. AlOOH releases water, and adding 5 wt.% AlOOH crucially influences thermal decomposition by enhancing the hydrolysis of PC and ofThe influence of nano-dispersed 5 wt.% boehmite (AlOOH) and 5 wt.% AlOOH combined with bisphenol A bis(diphenyl phosphate) (BDP) in bisphenol A polycarbonate/acrylonitrile–butadiene–styrene (PC/ABS) + poly(tetrafluoroethylene) (PTFE), and 1 wt.% AlOOH with and without BDP, resorcinol bis(diphenyl phosphate) (RDP), and triphenyl phosphate (TPP), on PC/ABS + PTFE has been investigated. Possible flame retardancy mechanisms are revealed. Thermogravimetry (TG) and evolved gas analysis (TG-FTIR) are used to study pyrolysis, a cone calorimeter applying different external heat fluxes is used to investigate fire behaviour, and LOI and UL 94 are used to investigate flammability. Fire residues were investigated using ATR-FTIR. Adding 5 wt.% AlOOH decreases the peak heat release rate, as also has been reported for polymer nanocomposites with other layered structures. AlOOH releases water, and adding 5 wt.% AlOOH crucially influences thermal decomposition by enhancing the hydrolysis of PC and of BDP. For PC/ABS + PTFE + BDP + 5 wt.% AlOOH, the formation of AlPO4, for instance, results in antagonistic effects on the charring of PC + BDP, whereas synergy is observed in LOI. When only 1 wt.% AlOOH is added to the PC/ABS + PTFE with and without BDP, RDP and TPP, respectively, no significant influence is observed on thermal decomposition, UL 94, LOI or performance in the cone calorimeter.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Kristin Pawlowski, Bernhard SchartelORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer degradation and stability
Jahr der Erstveröffentlichung:2008
Verlag:Applied Science Publ.
Verlagsort:London
Jahrgang/Band:93
Ausgabe/Heft:3
Erste Seite:657
Letzte Seite:667
Freie Schlagwörter:Aryl phosphates; Boehmite; Flame retardant; Flammability; Nanocomposites; PC/ABS
DOI:10.1016/j.polymdegradstab.2008.01.002
ISSN:0141-3910
ISSN:1873-2321
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:31.03.2008
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.