Thermal desoprtion analysis of hydrogen trapping in micro-alloyed high strength steels
- Hydrogen can cause unexpected material failure under consideration of stresses (external/internal) during manufacturing, processing or service of the materials. This failure is mostly based on a certain degradation of the mechanical properties. Thus, the correlation of hydrogen trapping vs. a respective microstructure is necessary for high strength steels. Thus, the scope of this work is the improvement of existing hydrogen trap models by verification of activation energies for hydrogen traps as well as the influence of the determination method. In this scope, the thermal desorption method is appropriate to distinguish between different hydrogen traps. Nevertheless, the specimen temperature has to be accounted very carefully in case of calculating the necessary trap energy.
Autor*innen: | Michael RhodeORCiD |
---|---|
Koautor*innen: | Enrico Steppan, Phillipp Mantzke, Thomas KannengießerORCiD |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2016 |
DDC-Klassifikation: | Naturwissenschaften und Mathematik / Chemie / Analytische Chemie |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten | |
Freie Schlagwörter: | Degradation; Heat treatment condition; High strength steels; Hydrogen trapping; Thermal desorption analysis (TDA) |
Veranstaltung: | IIW Intermediate Meeting, Meeting of commission II-A |
Veranstaltungsort: | Madrid, Spain |
Beginndatum der Veranstaltung: | 29.02.2016 |
Enddatum der Veranstaltung: | 03.03.2016 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 18.03.2016 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |