Ageing under Hydrogen: effects on O-ring seals
- In this work we present results for three typical sealing materials (EPDM, HNBR, FKM) after up to 100 days ageing at high temperature under hydrogen. To allow for a better evaluation of the occurring changes the results are compared with effects of ageing in air on the material properties. Despite the common assumption that ageing under hydrogen atmosphere is expected to be less severe for the material in com-parison to air ageing, this is not seen for every material.
Autor*innen: | Matthias JaunichORCiD |
---|---|
Koautor*innen: | Anja Kömmling, Maha Zaghdoudi |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2023 |
Organisationseinheit der BAM: | 3 Gefahrgutumschließungen; Energiespeicher |
3 Gefahrgutumschließungen; Energiespeicher / 3.4 Sicherheit von Lagerbehältern | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik |
Freie Schlagwörter: | Ageing; Compression set; Hydrogen; Seal |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
Energie / Wasserstoff | |
Veranstaltung: | Technomer 2023 |
Veranstaltungsort: | Chemnitz, Germany |
Beginndatum der Veranstaltung: | 09.11.2023 |
Enddatum der Veranstaltung: | 10.11.2023 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 14.11.2023 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |