Correlation between crack propagation rate and cure process of epoxy resins

  • Fracture mechanics approaches are increasingly applied for the characterization of epoxy resin and adhesive mechanical properties. Therefore, the fracture toughness and crack resistance under static load ISO 13586 [1] are often regarded as state of the art to analyse material improvements. However, experimental investigations on fatigue behaviour, thus the crack propagation according to ISO 15850 [2], seem to be much more sensitive to characterize the materials for in service loading conditions. Firstly, an efficient testing concept was developed at BAM. In this framework, the geometry for a modified single edge notched tensile specimen (SET) was developed in order to assure appropriate resolution in measuring the crack length via a CCD-camera [3]. In the next step, the influence of the cure temperature on the fracture-mechanical properties was investigated.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Volker Trappe, Stephan Günzel, Matthias Jaunich
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer testing
Jahr der Erstveröffentlichung:2012
Verlag:Elsevier Science
Verlagsort:Amsterdam [u.a.]
Jahrgang/Band:31
Ausgabe/Heft:5
Erste Seite:654
Letzte Seite:659
Freie Schlagwörter:Crack propagation; Crack resistance; Fracture mechanics; Fracture toughness; Plastics
DOI:https://doi.org/10.1016/j.polymertesting.2012.03.007
ISSN:0142-9418
Verfügbarkeit des Volltexts:Papiergebundenes Belegexemplar in der Bibliothek der BAM vorhanden ("Hard-copy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:12.11.2012