- Four hundred sixteen silver coins stemming from the Ottoman Empire (16th and 17th centuries) were analyzed in order to confirm the fineness of the coinage as well as to study the provenance of the alloy used for the coins. As most of the coins showed the typical green patina on their surfaces due to corrosion processes which have led to the depletion of copper in the near-surface domains of the silver coins in comparison to their core composition, small samples by cutting splinters from the coins had to be taken, embedded in synthetic resin and cross-sectioned in order to investigate the true-heart metal composition. The type of the alloy was investigated as well as if coins minted in different locations demonstrated homogeneous traits concerning the predominant impurities which could suggest a common ore. Several X-ray based techniques (µ-XRF, µ-SRXRF and µ-PIXE) could be applied in order to determine the silver contents as well as the minor and trace elements. Finally, SEM/EDX wasFour hundred sixteen silver coins stemming from the Ottoman Empire (16th and 17th centuries) were analyzed in order to confirm the fineness of the coinage as well as to study the provenance of the alloy used for the coins. As most of the coins showed the typical green patina on their surfaces due to corrosion processes which have led to the depletion of copper in the near-surface domains of the silver coins in comparison to their core composition, small samples by cutting splinters from the coins had to be taken, embedded in synthetic resin and cross-sectioned in order to investigate the true-heart metal composition. The type of the alloy was investigated as well as if coins minted in different locations demonstrated homogeneous traits concerning the predominant impurities which could suggest a common ore. Several X-ray based techniques (µ-XRF, µ-SRXRF and µ-PIXE) could be applied in order to determine the silver contents as well as the minor and trace elements. Finally, SEM/EDX was applied in order to study the homogeneity/heterogeneity of the coins and the presence of surface enrichments. In general, the silver content of the analyzed specimen varies between 90% and 95%. These outcomes have not supported the historical interpretations, which predict that during the period studied a debasement of approximately 44% of the silver content of the coins should have occurred.…
![zeige mehr zeige mehr](/opus4-bam/layouts/opus4/img/arrow_down.png)
![zeige weniger zeige weniger](/opus4-bam/layouts/opus4/img/arrow_up.png)