Thin Sol-Gel Alumina Coating as Protection of a 9% Cr Steel Against Flue Gas Corrosion at 650 °C
- Samples of sol-gel alumina coated and uncoated P92 steel were exposed to flue gas at 650 °C for 300 h. As result of this treatment a 50 µm thick bi-layered oxide scale had formed on the surface of the uncoated sample. Below the scale a 40 µm thick inner oxidation zone was detected. In contrast, the porous, micron thick alumina coating enabled the formation of a chromium oxide scale with a thickness of some nanometers at the interface between steel substrate and coating. In this case high temperature corrosion of the steel was prevented so far.
Autor*innen: | Marianne NofzORCiD, Ilona Dörfel, Regine Sojref, Nicole Wollschläger, Maria Mosquera Feijoo, Wencke Schulz, Axel KranzmannORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Oxidation of Metals |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
5 Werkstofftechnik / 5.6 Glas | |
Verlag: | Springer |
Jahrgang/Band: | 89 |
Ausgabe/Heft: | 3-4 |
Erste Seite: | 453 |
Letzte Seite: | 470 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik |
Freie Schlagwörter: | High-temperature corrosion; Oxide coatings; SEM; Steel; TEM |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
DOI: | 10.1007/s11085-017-9799-0 |
ISSN: | 0030-770X |
ISSN: | 1573-4889 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 15.03.2018 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 29.03.2018 |