Corrosion and passivation of AlCrFe2Ni2Mox high-entropy alloys in sulphuric acid
- Corrosion behaviour of AlCrFe2Ni2Mox (x = 0.0, 0.1, 0.15, 0.3 and 0.6) high-entropy alloys was investigated in a 0.1 M H2SO4 solution. Passive films formed upon anodic polarisation, built of Al-based inner layer and (Cr, Fe, Mo)-based outer layer, had good protective properties. In particular, they prevented corrosion of the (Al, Ni)-rich BCC-B2 phase, which was observed under open-circuit conditions. Moderate amounts of Mo, up to x = 0.3, positively affected the passivation ability of AlCrFe2Ni2. Significant changes in microstructure and phase composition of the alloy at higher Mo concentrations (x = 0.6) resulted in deterioration of its corrosion resistance.
Autor*innen: | Jakub Czerski, Marzena Mitoraj-Krolikowska, Elzbieta Godlewska, Annica Wetzel, Julia Witt, Ozlem Ozcan, Mateusz Marzec, Marcin Goly |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Corrosion Science |
Jahr der Erstveröffentlichung: | 2024 |
Organisationseinheit der BAM: | 6 Materialchemie |
6 Materialchemie / 6.2 Material- und Oberflächentechnologien | |
Verlag: | Elsevier Ltd. |
Jahrgang/Band: | 229 |
Aufsatznummer: | 111855 |
Erste Seite: | 1 |
Letzte Seite: | 17 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | AFM; Acid corrosion; Alloy; EIS; Passive films; Sulphuric acid |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.1016/j.corsci.2024.111855 |
ISSN: | 0010-938X |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 20.03.2024 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 20.03.2024 |