Low temperature synthesis of monodisperse nanoscaled ZrO2 with a large specific surface area

  • Thermal decomposition of Zr(C2O4)2·4H2O within an autoclave or in a conventional tube furnace at temperatures below 380 °C resulted in nano- and micron-sized ZrO2, respectively. Reactions under autogenic pressure yielded monodisperse monoclinic (m) and tetragonal (t) ZrO2 nanoparticles with an average diameter of ~8 nm and interconnected t-ZrO2 nanoparticles with diameters of ~4 nm, depending on the synthesis temperature. Samples were characterised by X-ray diffraction (XRD), small angle X-ray scattering (SAXS), scanning electron microscopy (SEM), transmission electron microscopy (TEM) associated with energy dispersive X-ray spectroscopy (EDS), Raman microspectroscopy and photoluminescence spectroscopy (PL). Nanostructured zirconia materials exhibited high specific areas of 276–385 m2 g-1 which make them promising candidates as catalysts and catalyst supports. Co-existence of m- and t-ZrO2 nanoparticles with diameters of 6–9 nm, i.e. above the critical particle size of 6 nm for theThermal decomposition of Zr(C2O4)2·4H2O within an autoclave or in a conventional tube furnace at temperatures below 380 °C resulted in nano- and micron-sized ZrO2, respectively. Reactions under autogenic pressure yielded monodisperse monoclinic (m) and tetragonal (t) ZrO2 nanoparticles with an average diameter of ~8 nm and interconnected t-ZrO2 nanoparticles with diameters of ~4 nm, depending on the synthesis temperature. Samples were characterised by X-ray diffraction (XRD), small angle X-ray scattering (SAXS), scanning electron microscopy (SEM), transmission electron microscopy (TEM) associated with energy dispersive X-ray spectroscopy (EDS), Raman microspectroscopy and photoluminescence spectroscopy (PL). Nanostructured zirconia materials exhibited high specific areas of 276–385 m2 g-1 which make them promising candidates as catalysts and catalyst supports. Co-existence of m- and t-ZrO2 nanoparticles with diameters of 6–9 nm, i.e. above the critical particle size of 6 nm for the formation of t-ZrO2, demonstrated that the particle size is not the only factor for stabilisation of the t-ZrO2 modification at room temperature.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:N. Zink, Franziska EmmerlingORCiD, T. Häger, M. Panthöfer, M.N. Tahir, U. Kolb, W. Tremel
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Dalton transactions
Jahr der Erstveröffentlichung:2013
Herausgeber (Institution):Royal Society of Chemistry
Verlag:RSC
Verlagsort:Cambridge
Jahrgang/Band:42
Erste Seite:432
Letzte Seite:440
DOI:10.1039/c2dt12496c
ISSN:1477-9226
ISSN:1477-9234
ISSN:1364-5447
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:22.02.2013
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.