Novel DOPO-based flame retardants in high-performance carbon fibre epoxy composites for aviation

  • Two novel, halogen-free, phosphorus-based oligomeric flame retardants are investigated in the commercial epoxy resin RTM6 and ~70 wt.% carbon fibre RTM6 composites (RTM6-CF) with respect to pyrolysis and fire behaviour. The flame retardants are based on 9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide (DOPO) units linked to the star-shaped aliphatic ground body tetra-[(acryloyloxy)ethyl] pentarythrit (DOPP), or heterocyclic tris-[(acryloyloxy)ethyl] isocyanurate (DOPI), respectively. The glass transition temperature is reduced by adding DOPP and DOPI, but the mechanical properties of the composites (e.g. interlaminar shear strength (ILSS) and Gc in mode I and II) remain unchanged. Decomposition models are proposed based on mass loss, evolved gas analysis (TG–FTIR) and condensed product analysis (hot stage cell within FTIR). The fire behaviour is investigated comprehensively (UL 94, limiting oxygen index (LOI) and cone calorimeter). Both flame retardants act in the gas phase throughTwo novel, halogen-free, phosphorus-based oligomeric flame retardants are investigated in the commercial epoxy resin RTM6 and ~70 wt.% carbon fibre RTM6 composites (RTM6-CF) with respect to pyrolysis and fire behaviour. The flame retardants are based on 9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide (DOPO) units linked to the star-shaped aliphatic ground body tetra-[(acryloyloxy)ethyl] pentarythrit (DOPP), or heterocyclic tris-[(acryloyloxy)ethyl] isocyanurate (DOPI), respectively. The glass transition temperature is reduced by adding DOPP and DOPI, but the mechanical properties of the composites (e.g. interlaminar shear strength (ILSS) and Gc in mode I and II) remain unchanged. Decomposition models are proposed based on mass loss, evolved gas analysis (TG–FTIR) and condensed product analysis (hot stage cell within FTIR). The fire behaviour is investigated comprehensively (UL 94, limiting oxygen index (LOI) and cone calorimeter). Both flame retardants act in the gas phase through flame inhibition and in the condensed phase through charring. The UL 94 of RTM6 is improved from HB to V-1 and V-0; the LOI from 25% to 34–38%. Peak heat release rate (PHRR) and total heat evolved (THE) are lowered by 31-49% and 40–44%, respectively. Adding CF increases the residue, reduces the THE, but suppresses the charring due to RTM6 and flame retardants. Thus the THE of RTM6-CF is reduced by about 25% when DOPI and DOPP are added. However, UL 94: V-0 and LOI of 45% and 48% are achieved with ~0.6 wt.% phosphorus.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 1-s2.0-S0014305711000619-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Birgit Perret, Bernhard SchartelORCiD, K. Stöß, M. Ciesielski, J. Diederichs, M. Döring, J. Krämer, V. Altstädt
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):European polymer journal
Jahr der Erstveröffentlichung:2011
Verlag:Elsevier Ltd.
Verlagsort:Oxford
Jahrgang/Band:47
Ausgabe/Heft:5
Erste Seite:1081
Letzte Seite:1089
Freie Schlagwörter:Carbon fibre reinforced composites; DOPO; Epoxy resin (RTM6); Flame retardancy; Mechanical properties
DOI:10.1016/j.eurpolymj.2011.02.008
ISSN:0014-3057
ISSN:1873-1945
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:18.04.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.